绿点现货 基础创新塑料(日本) PBT 310SEO-1001 阻燃级 家电部件 开关 线轴
绿点现货 基础创新塑料(日本) PBT 310SEO-1001 阻燃级 家电部件 开关 线轴
Polybutylene Terephthalate
SABIC Innovative Plastics
产品说明：
VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.
物性信息：
| 黄卡编号 | E121562-220784 |
| 特性 | 阻燃性 |
| 用途 | 电气/电子应用领域 家电部件 开关 外壳 线轴 |
| 加工方法 | 注射成型 |
| 多点数据 | Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) |
| 比重 | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| 特定体积 | 0.710 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） (250°C/2.16 kg) | 8.6 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (250°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 1 | 1.1 到 1.8 | % | 内部方法 |
| 流动 2 | 1.5 到 2.3 | % | 内部方法 |
| 流动 3 | 0.90 到 1.6 | % | 内部方法 |
| 流动 : 3.20 mm | 1.5 到 2.3 | % | 内部方法 |
| 横向流动 4 | 0.90 到 1.9 | % | 内部方法 |
| 横向流动 5 | 1.0 到 1.7 | % | 内部方法 |
| 横向流动 6 | 1.6 到 2.4 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.36 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.080 | % | ISO 62 |
| 洛氏硬度 (R 计秤) | 120 | ISO 2039-2 | |
| 球压硬度 (H 358/30) | 105 | MPa | ISO 2039-1 |
| 拉伸模量 | |||
| -- 7 | 2820 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 8 | 58.0 | MPa | ASTM D638 |
| 屈服 | 55.0 | MPa | ISO 527-2/50 |
| 断裂 9 | 58.0 | MPa | ASTM D638 |
| 断裂 | 40.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 10 | 20 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/50 |
| 断裂 11 | 20 | % | ASTM D638 |
| 断裂 | 20 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 12 | 2620 | MPa | ASTM D790 |
| -- 13 | 2600 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 90.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 14 | 101 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 19.0 | mg | 内部方法 |
| 简支梁缺口冲击强度 | |||
| -30°C 15 | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C 16 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/2C |
| 简支梁无缺口冲击强度 17 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 22 | J/m | ASTM D256 |
| 23°C | 37 | J/m | ASTM D256 |
| -30°C 18 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 19 | 5.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| -30°C 20 | 无断裂 | ISO 180/1U | |
| 23°C 21 | 无断裂 | ISO 180/1U | |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 200 | J | ASTM D3763 |