高流动 PBT 基础创新塑料(美国) K4560-BK1066 抗冲击 玻纤增强 耐水解 工程塑料
观看高流动 PBT 基础创新塑料(美国) K4560-BK1066 抗冲击 玻纤增强 耐水解 工程塑料视频：
高流动 PBT 基础创新塑料(美国) K4560-BK1066 抗冲击 玻纤增强 耐水解 工程塑料
Polybutylene Terephthalate
SABIC Innovative Plastics
30% 玻璃纤维增强材料
产品说明：
30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
物性信息：
| 填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
| 添加剂 | 冲击改性剂 |
| 特性 | 冲击改性 流动性高 水解稳定 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) |
| 比重 | 1.50 | g/cm³ | ASTM D792 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.60 到 0.80 | % | 内部方法 |
| 横向流动 : 3.20 mm | 1.0 到 1.2 | % | 内部方法 |
| 拉伸模量 1 | 8840 | MPa | ASTM D638 |
| 抗张强度 | ASTM D638 | ||
| 屈服 2 | 112 | MPa | ASTM D638 |
| 断裂 | 107 | MPa | ASTM D638 |
| 断裂 | 115 | MPa | ASTM D638 |
| 断裂 | 110 | MPa | ASTM D638 |
| 断裂 3 | 112 | MPa | ASTM D638 |
| 断裂 | 102 | MPa | ASTM D638 |
| 断裂 | 96.0 | MPa | ASTM D638 |
| 伸长率 4 | ASTM D638 | ||
| 屈服 5 | 4.0 | % | ASTM D638 |
| 屈服 | 3.0 | % | ASTM D638 |
| 断裂 6 | 2.5 | % | ASTM D638 |
| 断裂 | 3.0 | % | ASTM D638 |
| 断裂 7 | 4.0 | % | ASTM D638 |
| 断裂 8 | 2.2 | % | ASTM D638 |
| 弯曲模量 9 | ASTM D790 | ||
| 50.0 mm 跨距 10 | 7100 | MPa | ASTM D790 |
| 50.0 mm 跨距 11 | 7500 | MPa | ASTM D790 |
| 50.0 mm 跨距 12 | 8000 | MPa | ASTM D790 |
| 50.0 mm 跨距 | 7200 | MPa | ASTM D790 |
| 50.0 mm 跨距 13 | 7400 | MPa | ASTM D790 |
| 弯曲强度 14(断裂, 50.0 mm 跨距) | 173 | MPa | ASTM D790 |
| 弯曲应变 - 1.3 mm/min, 50 mm span | ASTM D790 | ||
| -- 15 | 4.2 | % | ASTM D790 |
| -- 16 | 4.2 | % | ASTM D790 |
| -- 17 | 4.5 | % | ASTM D790 |
| -- 18 | 4.0 | % | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C) | 96 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 820 | J/m | ASTM D4812 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| 23°C, Total Energy 19 | 6.10 | J | ASTM D3763 |
| 23°C, Total Energy 20 | 7.56 | J | ASTM D3763 |
| 23°C, Total Energy 21 | 8.81 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 3.20 mm | 220 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 200 | °C | ASTM D648 |
| 干燥温度 | 60.0 到 76.7 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 干燥时间，Zui大 | 8.0 | hr | |
| 建议的Zui大水分含量 | 0.050 | % | |
| 建议注射量 | 40 到 80 | % | |
| 料筒后部温度 | 238 到 254 | °C | |
| 料筒中部温度 | 243 到 260 | °C | |
| 料筒前部温度 | 249 到 266 | °C |
展开全文