Polycarbonate
SABIC Innovative Plastics
产品说明:
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing, Wear Resistant.
Also known as: LNP* LUBRILOY* Compound D-EP
Product reorder name: D2000P
物性信息:
黄卡编号 | E121562-101283868 |
添加剂 | 润滑剂 |
特性 | 可加工性,良好 耐磨损性良好 润滑 |
加工方法 | 注射成型 |
比重 | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 | |||
流动 : 24小时 | 0.80 | % | ASTM D955 |
横向流动 : 24小时 | 0.80 | % | ASTM D955 |
垂直流动方向 : 24小时 | 0.81 | % | ISO 294-4 |
流动方向 : 24小时 | 0.84 | % | ISO 294-4 |
吸水率 | |||
24 hr, 50% RH | 0.14 | % | ASTM D570 |
平衡, 23°C, 50% RH | 0.21 | % | ISO 62 |
拉伸模量 | |||
-- 1 | 1930 | MPa | ASTM D638 |
-- | 2100 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 | 56.4 | MPa | ASTM D638 |
屈服 | 54.3 | MPa | ISO 527-2 |
断裂 | 46.4 | MPa | ASTM D638 |
断裂 | 46.1 | MPa | ISO 527-2 |
伸长率 | |||
屈服 | 5.9 | % | ASTM D638 |
屈服 | 5.3 | % | ISO 527-2 |
断裂 | 42 | % | ASTM D638 |
断裂 | 43 | % | ISO 527-2 |
弯曲模量 | |||
-- | 2280 | MPa | ASTM D790 |
-- | 2300 | MPa | ISO 178 |
-- | 86.7 | MPa | ASTM D790 |
-- | 86.0 | MPa | ISO 178 |
摩擦系数 | ASTM D3702 Modified | ||
与自身 - 动态 | 0.19 | ASTM D3702 Modified | |
与自身 - 静态 | 0.16 | ASTM D3702 Modified | |
磨损因数 - Washer | 44.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
悬壁梁缺口冲击强度 | |||
23°C | 450 | J/m | ASTM D256 |
23°C 2 | 13 | kJ/m² | ISO 180/1A |
无缺口悬臂梁冲击 | |||
23°C | 无断裂 | ASTM D4812 | |
23°C 3 | 140 | kJ/m² | ISO 180/1U |
装有测量仪表的落镖冲击 | |||
23°C, Energy at Peak Load | 40.3 | J | ASTM D3763 |
-- | 43.3 | J | ISO 6603-2 |
载荷下热变形温度 | |||
0.45 MPa, 未退火, 3.20 mm | 138 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 126 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 4 | 131 | °C | ISO 75-2/Af |
线形热膨胀系数 | ASTM E831, ISO 11359-2 | ||
流动 : -40 到 40°C | 7.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
横向 : -40 到 40°C | 7.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |