增强级PC 基础创新塑料 4019 高刚性 易流动 延展性 室外应用
Polycarbonate
SABIC Innovative Plastics
9.0% 玻璃纤维增强材料
产品说明：
LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only.
物性信息：
| 填料/增强材料 | 玻璃纤维增强材料, 9.0% 填料按重量 |
| 特性 | 刚性，良好 共聚物 可加工性，良好 快的成型周期 流动性中等 延展性 |
| 外观 | 不透明 可用颜色 |
| 加工方法 | 注射成型 |
| 比重 | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 7.5 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 6.50 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.20 到 0.60 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.20 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.15 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.40 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 3950 | MPa | ASTM D638 |
| -- | 3900 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 55.0 | MPa | ASTM D638 |
| 屈服 | 54.0 | MPa | ISO 527-2/5 |
| 断裂 3 | 45.0 | MPa | ASTM D638 |
| 断裂 | 48.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服 4 | 4.3 | % | ASTM D638 |
| 屈服 | 4.3 | % | ISO 527-2/5 |
| 断裂 5 | 14 | % | ASTM D638 |
| 断裂 | 8.7 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距 6 | 3500 | MPa | ASTM D790 |
| -- 7 | 3450 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 98.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 103 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 25 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 10 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 350 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 25 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 13 | ISO 180/1U | ||
| -30°C | 无断裂 | ISO 180/1U | |
| 23°C | 无断裂 | ISO 180/1U | |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距 14 | 135 | °C | ISO 75-2/Ae |
| 维卡软化温度 | 146 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 15 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| 线形热膨胀系数 | ASTM E831, ISO 11359-2 | ||
| 流动 : -40 到 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |