注塑级PC 基础创新塑料 LUX9616 阻燃 易流动 薄壁制品
![](http://img.11467.com/2023/07-12/1748566664.jpg)
注塑级PC 基础创新塑料 LUX9616 阻燃 易流动 薄壁制品
Polycarbonate
SABIC Innovative Plastics Asia Pacific
产品说明:
Lexan LUX9616 is a flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effective and thin wall FR performance. It intended to meet WEEE/RoHS re for various applications.
物性信息:
黄卡编号 | E207780-100792480 |
添加剂 | 阻燃性 |
特性 | Chlorine Free 良好的流动性 无溴 阻燃性 |
用途 | 薄壁部件 |
RoHS 合规性 | RoHS 合规 |
加工方法 | 注射成型 |
比重 | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
熔流率(熔体流动速率) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.60 到 0.80 | % | 内部方法 |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.35 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.15 | % | ISO 62 |
拉伸模量 | |||
-- 1 | 2300 | MPa | ASTM D638 |
-- | 2230 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 2 | 62.0 | MPa | ASTM D638 |
屈服 | 62.0 | MPa | ISO 527-2/50 |
断裂 3 | 65.0 | MPa | ASTM D638 |
断裂 | 58.0 | MPa | ISO 527-2/50 |
伸长率 | |||
屈服 4 | 6.0 | % | ASTM D638 |
屈服 | 6.0 | % | ISO 527-2/50 |
断裂 5 | 80 | % | ASTM D638 |
断裂 | 75 | % | ISO 527-2/50 |
弯曲模量 | |||
50.0 mm 跨距 6 | 2160 | MPa | ASTM D790 |
-- 7 | 2250 | MPa | ISO 178 |
弯曲应力 | |||
-- | 95.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 8 | 95.0 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | |||
23°C | 150 | J/m | ASTM D256 |
23°C 9 | 15 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
热变形温度 | |||
0.45 MPa, 未退火, 64.0 mm 跨距 10 | 135 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火, 3.20 mm | 125 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 11 | 125 | °C | ISO 75-2/Af |
维卡软化温度 | 141 | °C | ASTM D1525 12 |
Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
线形热膨胀系数 | ASTM E831 | ||
流动 : -40 到 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
横向 : -40 到 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
相比耐漏电起痕指数(CTI) | PLC 3 | UL 746 | |
高电弧燃烧指数(HAI) | PLC 1 | UL 746 | |
热丝引燃 (HWI) | PLC 3 | UL 746 |
UL 阻燃等级 (1.50 mm) | V-0 | UL 94 | |
灼热丝易燃指数 (1.00 mm) | 960 | °C | IEC 60695-2-12 |
热灯丝点火温度 | IEC 60695-2-13 | ||
1.00 mm | 850 | °C | IEC 60695-2-13 |
1.50 mm | 850 | °C | IEC 60695-2-13 |