抗化学 PPA 美国索尔维 AT-1125HS 冲击改性 耐高温 家电部件 燃料管线
抗化学 PPA 美国索尔维 AT-1125HS 冲击改性 耐高温 家电部件 燃料管线
Amodel® AT-1125 HS
Polyphthalamide
Solvay Specialty Polymers
25% 玻璃纤维增强材料
产品说明：
Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass-reinforced PPA.
Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly.
Black: AT-1125 HS BK 324
物性信息：
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 密度 | 1.35 | -- | g/cm³ | ISO 1183/A |
| 收缩率 | ASTM D955 | |||
| 流动 | 0.40 | -- | % | ASTM D955 |
| 横向流动 | 0.60 | -- | % | ASTM D955 |
| 吸水率 (24 hr) | 0.20 | -- | % | ASTM D570 |
| 拉伸模量 | ||||
| -- | 8480 | -- | MPa | ASTM D638 |
| -- | 8890 | -- | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 断裂 | 174 | -- | MPa | ASTM D638 |
| 断裂 | 190 | -- | MPa | ISO 527-2 |
| 伸长率 | ||||
| 断裂 | 3.2 | -- | % | ASTM D638 |
| 断裂 | 2.5 | -- | % | ISO 527-2 |
| 弯曲模量 | ||||
| -- | 7580 | 7580 | MPa | ASTM D790 |
| -- | 7790 | -- | MPa | ISO 178 |
| 弯曲应力 | ||||
| -- | 240 | -- | MPa | ISO 178 |
| 屈服 | 255 | 200 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 | 8.8 | -- | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | ||||
| -- | 120 | 85 | J/m | ASTM D256 |
| -- | 8.8 | -- | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | 1100 | 800 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | |||
| Energy as Maximum Load 1 | -- | 1.90 | J | ASTM D3763 |
| Total Energy | -- | 9.36 | J | ASTM D3763 |
| 总能量 | 13.8 | -- | J | ASTM D3763 |
| Zui大负载能量 2 | 2.03 | -- | J | ASTM D3763 |
| 载荷下热变形温度 | ||||
| 0.45 MPa, 未退火 | 279 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 235 | -- | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 280 | -- | °C | ISO 75-2/A |
| 熔融温度 | 311 | -- | °C | ISO 11357-3, ASTM D3418 |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的Zui大水分含量 | 0.10 | % | |
| 料斗温度 | 79.4 | °C | |
| 料筒后部温度 | 304 到 318 | °C | |
| 料筒前部温度 | 316 到 329 | °C | |
| 加工（熔体）温度 | 321 到 343 | °C | |
| 模具温度 | 135 | °C |