现货 PPO基础创新塑料(上海) ZX08309 高介电常数 矿物填充
![](http://static.11467.com/img/ab-prev-0.png)
![](http://img2.11467.com/2023/10-13/1008770898_small.jpg)
![](http://img2.11467.com/2023/10-13/1008770898_small.jpg)
![](http://img2.11467.com/2023/10-12/2537380563_small.jpg)
![](http://img.11467.com/2023/10-12/2527513652_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-06-16 07:00:00
价格:请来电询价
品牌:PPO塑胶原料
型号:ZX08309
特性:高介电常数 矿物填充
联系电话:0755-21047619
联系手机:18819106372
联系人:刘春梅
让卖家联系我
详细介绍
现货 PPO基础创新塑料(上海) ZX08309 高介电常数 矿物填充
LNP™ THERMOCOMP™ ZX08309 compound
Polyphenylene Ether + PS
SABIC Innovative Plastics Asia Pacific
矿物填料
产品说明:
This material is mineral filled PPO grade with high dielectric constant and low loss tangent
物性信息:
填料/增强材料 |
|
加工方法 |
|
密度 | 1.66 | g/cm³ | ISO 1183 |
溶化体积流率(MVR) (300°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
收缩率 | ASTM D955 | ||
流动 : 24小时 | 0.70 | % | ASTM D955 |
横向流动 : 24小时 | 0.65 | % | ASTM D955 |
弯曲模量 1 | 3200 到 3500 | MPa | ISO 178 |
弯曲强度 2(断裂, 50.0 mm 跨距) | 90.0 到 100 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (23°C) | 60 | J/m | ASTM D256 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火, 3.20 mm | 134 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 122 | °C | ASTM D648 |
介电常数 (1.10 GHz) | 4.40 到 4.60 | ASTM ES7-83 | |
耗散因数 (1.10 GHz) | 2.0E-3 到 4.0E-3 | ASTM ES7-83 |
干燥温度 | 105 | °C | |
干燥时间 | 3.0 到 5.0 | hr | |
料筒后部温度 | 280 到 285 | °C | |
料筒中部温度 | 290 到 295 | °C | |
料筒前部温度 | 300 到 305 | °C | |
射嘴温度 | 290 到 295 | °C | |
加工(熔体)温度 | 295 到 305 | °C | |
模具温度 | 90.0 | °C | |
背压 | 9.00 | MPa | |
螺杆转速 | 100 | rpm |
现货 PPO基础创新塑料(上海) ZX08309 高介电常数 矿物填充
现货 PPO基础创新塑料(上海) ZX08309 高介电常数 矿物填充
相关产品
联系方式
- 地址:深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话:0755-21047619
- 销售经理:刘春梅
- 手机:18819106372
- 传真:暂无
- 微信:18819106372
- QQ:241813087
- Email:241813087@qq.com
产品分类
站内搜索