Makrolon® 阻燃级 上海科思创(拜耳)PC 6487 中等粘性 脱模级 抗UV
![](http://static.11467.com/img/ab-prev-0.png)
![](http://img2.11467.com/2023/09-28/2183570885_small.jpg)
![](http://img2.11467.com/2023/09-28/2183570885_small.jpg)
![](http://img2.11467.com/2023/09-28/2174939672_small.jpg)
![](http://img.11467.com/2023/09-28/2177049952_small.jpg)
![](http://static.11467.com/img/ab-next-0.png)
更新时间:2024-07-01 07:00:00
价格:请来电询价
品牌:PC塑胶原料
型号:6487
特性:中等粘性 脱模级 抗UV
联系电话:0755-21047619
联系手机:18819106372
联系人:刘春梅
让卖家联系我
详细介绍
Makrolon® 阻燃级 上海科思创(拜耳)PC 6487 中等粘性 脱模级 抗UV
Makrolon® 6487
Polycarbonate
Covestro - Polycarbonates
产品说明:
MVR (300 °C/1.2 kg) 9.0 cm³/10 min; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; medium viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; available in opaque colors only
物性信息:
黄卡编号 |
|
添加剂 |
|
特性 |
|
RoHS 合规性 |
|
外观 |
|
加工方法 |
|
密度 (23°C) | 1.20 | g/cm³ | ISO 1183 |
表观密度 1 | 0.64 | g/cm³ | ISO 60 |
熔流率(熔体流动速率) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
收缩率 | |||
垂直流动方向 | 0.60 到 0.80 | % | ISO 2577 |
流动方向 | 0.60 到 0.80 | % | ISO 2577 |
垂直流动方向 : 2.00 mm 2 | 0.75 | % | ISO 294-4 |
流动方向 : 2.00 mm 3 | 0.70 | % | ISO 294-4 |
吸水率 | ISO 62 | ||
饱和, 23°C | 0.30 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.12 | % | ISO 62 |
球压硬度 | 117 | MPa | ISO 2039-1 |
拉伸模量 (23°C) | 2450 | MPa | ISO 527-2/1 |
拉伸应力 | ISO 527-2/50 | ||
屈服, 23°C | 66.0 | MPa | ISO 527-2/50 |
断裂, 23°C | 65.0 | MPa | ISO 527-2/50 |
拉伸应变 | ISO 527-2/50 | ||
屈服, 23°C | 6.0 | % | ISO 527-2/50 |
断裂, 23°C | 120 | % | ISO 527-2/50 |
标称拉伸断裂应变 (23°C) | > 50 | % | ISO 527-2/50 |
弯曲模量 4(23°C) | 2450 | MPa | ISO 178 |
弯曲应力 5 | ISO 178 | ||
3.5% 应变, 23°C | 75.0 | MPa | ISO 178 |
23°C | 99.0 | MPa | ISO 178 |
Flexural Strain at Flexural Strength 6(23°C) | 7.0 | % | ISO 178 |
Application of Flame from Small Burner - Method K and F (2.00 mm) | K1, F1 | DIN 53438-1, -3 | |
Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 | |
Flash Ignition Temperature | 470 | °C | ASTM D1929 |
Self Ignition Temperature | 550 | °C | ASTM D1929 |
Electrolytical Corrosion (23°C) | A1 | IEC 60426 |
简支梁缺口冲击强度 7 | ISO 7391 | ||
-30°C, 完全断裂 | 12 | kJ/m² | ISO 7391 |
23°C, 局部断裂 | 70 | kJ/m² | ISO 7391 |
简支梁无缺口冲击强度 | ISO 179/1eU | ||
-30°C | 无断裂 | ISO 179/1eU | |
23°C | 无断裂 | ISO 179/1eU | |
悬壁梁缺口冲击强度 8 | ISO 7391 | ||
-30°C, 完全断裂 | 12 | kJ/m² | ISO 7391 |
23°C, 局部断裂 | 65 | kJ/m² | ISO 7391 |
多轴向仪器化冲击能量 | ISO 6603-2 | ||
-30°C | 55.0 | J | ISO 6603-2 |
23°C | 50.0 | J | ISO 6603-2 |
多轴向仪器化冲击力峰值 | ISO 6603-2 | ||
-30°C | 6000 | N | ISO 6603-2 |
23°C | 5200 | N | ISO 6603-2 |
相关产品
联系方式
- 地址:深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话:0755-21047619
- 销售经理:刘春梅
- 手机:18819106372
- 传真:暂无
- 微信:18819106372
- QQ:241813087
- Email:241813087@qq.com
产品分类
站内搜索