Ultramid® A3WG6 BK00564
Polyamide 66
BASF Corporation
30% 玻璃纤维增强材料
产品说明：
Ultramid A3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. A3EG6 is the preferred grade for producing electrically insulating parts.
Applications
Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.
物性信息：
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 密度 | 1.36 | g/cm³ | ISO 1183 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 5.5 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 1.7 | % | ISO 62 |
| 拉伸应力 (断裂, 23°C) | 179 | MPa | ISO 527-2 |
| 拉伸应变 (断裂, 23°C) | 2.6 | % | ISO 527-2 |
| 弯曲模量 (23°C) | 8730 | MPa | ISO 178 |
| 悬壁梁缺口冲击强度 (23°C) | 8.5 | kJ/m² | ISO 180 |
| 热变形温度 (1.8 MPa, 未退火) | 250 | °C | ISO 75-2/A |
| 溶融温度（DSC） | 260 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.710 mm | 125 | °C | UL 746 |
| 1.50 mm | 125 | °C | UL 746 |
| 3.00 mm | 125 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 115 | °C | UL 746 |
| 3.00 mm | 120 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 115 | °C | UL 746 |
| 3.00 mm | 130 | °C | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 0.710 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的Zui大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 280 到 305 | °C | |
| 模具温度 | 80.0 到 90.0 | °C | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 |
增强级 PA66 德国巴斯夫 A3WG6-BK 尺寸稳定 耐热 型材 汽车领域应用
德国巴斯夫pa66,A3WG6-BK ,增强级 PA66, 耐热级PA66,pa66塑胶原料
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com