低摩擦系数 PA9T日本可乐丽 G1302A 加纤30% 耐磨 无卤素聚酰胺9T
Genestar™ G1302A
Polyamide 9T
Kuraray Co., Ltd.
30% 玻璃纤维增强材料
产品说明：
The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability.
*'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.
物性信息：
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 比重 | 1.37 | g/cm³ | |
| 熔流率（熔体流动速率） (320°C/2.16 kg) | 46 | g/10 min | ASTM D1238 |
| 收缩率 | |||
| 流动 : 1.00 mm | 0.20 | % | |
| 横向流动 : 1.00 mm | 0.70 | % | |
| 吸水率 1(平衡, 40°C, 95%RH) | 1.4 | % |
| 抗张强度 | 165 | MPa | ASTM D638 |
| 伸长率 (断裂) | 4.0 | % | ASTM D638 |
| 弯曲模量 | 9000 | MPa | ASTM D790 |
| 弯曲强度 | 210 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | 120 | J/m | ASTM D256 |
| 载荷下热变形温度 (1.8 MPa, 未退火) | 290 | °C | ASTM D648 |
| 玻璃转化温度 | 125 | °C | |
| 熔融温度 | 306 | °C |
| 体积电阻率 | 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 | 30 | kV/mm | ASTM D149 |
| 介电常数 (10.0 GHz) | 3.30 | ASTM D150 | |
| 耗散因数 (10.0 GHz) | 9.0E-3 | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | PLC 0 | UL 746 |
| UL 阻燃等级 | HB | UL 94 |
| Bar Flow Length 2(320°C, 500.0 µm) | 5.50 | cm | |
| Weld Elongation | 0.70 | % | ASTM D638 |
| Weld Strength | 47.0 | MPa | ASTM D638 |
PA9T,日本可乐丽,G1302A ,低摩擦系数,玻纤增强,聚酰胺9T
PA9T,日本可乐丽,G1302A ,低摩擦系数,玻纤增强,聚酰胺9T
相关产品
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com
产品分类
站内搜索