LEXAN™基础创新塑料(南沙)PC 3412R-739 加纤20% 脱模 注塑成型
LEXAN™ 3412R resin
Polycarbonate
SABIC Innovative Plastics
20% 玻璃纤维增强材料
产品说明：
20% GR, provides improved mechanical properties and UL94 V-1 rated at 0.058". Internal mold release added.
物性信息：
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 加工方法 |
|
| 多点数据 |
|
| 比重 | ASTM D792 | ||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ASTM D792 |
| 特定体积 | 0.741 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 4.3 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.10 到 0.30 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.16 | % | ASTM D570 |
| 平衡, 23°C | 0.29 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 91 | ASTM D785 | |
| R 级 | 122 | ASTM D785 |
| 抗张强度 1(断裂) | 110 | MPa | ASTM D638 |
| 伸长率 2(断裂) | 5.0 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 5520 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 131 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 17.0 | mg | ASTM D1044 |
| 悬壁梁缺口冲击强度 (23°C) | 110 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 1000 | J/m | ASTM D4812 |
| 落锤冲击 (23°C) | 5.42 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 63.0 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 149 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 146 | °C | ASTM D648 |
| 维卡软化温度 | 166 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-40 到 95°C) | 2.7E-5 | cm/cm/°C | ASTM E831 |
| 比热 | 1170 | J/kg/°C | ASTM C351 |
| 导热系数 | 0.21 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 19 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 3.13 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 7.3E-3 | ASTM D150 | |
| 耐电弧性 7 | PLC 7 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 5 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 4 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 0 | UL 746 |
3412R-739,基础创新塑料PC,聚碳酸酯，增强级pc
3412R-739,基础创新塑料PC,聚碳酸酯，增强级pc
3412R-739,基础创新塑料PC,聚碳酸酯，增强级pc
相关产品
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com
产品分类
站内搜索