高冲击 美国杜邦 LCP 6330 矿物填充30% 阻燃V0 高热变形温度
发布：2024-02-29 14:01，更新：2024-05-21 07:00
高冲击 美国杜邦 LCP 6330 矿物填充30% 阻燃V0 高热变形温度
6330
液晶聚合物#|LCP
美国杜邦
物性信息：
| 比重 | 1.64 | ASTM D-792 | |
| 模具收缩率 (3.2mm(0.126in)) | 0.5 | % | ASTM D-955 |
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 弯曲模量 | ASTM D-790 |
| 弯曲模量 | ASTM D-790 | ||
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (3.2mm(0.125in),23℃(73℉)) | 9600 | MPa | |
| (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | |
| 拉伸模量 (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | ASTM D-638 |
| 拉伸强度 (1.6mm(0.063in),23℃(73℉)) | 141 | MPa | ASTM D-638 |
| 断裂伸长率 (1.6mm(0.063in),23℃(73℉)) | 3.3 | % | ASTM D-638 |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-790 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 断裂伸长率 (3.2mm(0.125in),23℃(73℉)) | 4 | % | ASTM D-638 |
| 拉伸模量 | ASTM D-638 | ||
| (3.2mm) | 10500 | MPa | |
| (1.6mm(0.063in),23℃(73℉)) | 11569 | MPa | |
| 压缩模量 | 4100 | MPa | ASTM D-695 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 弯曲模量 (0.8mm(0.032in),23℃(73℉)) | 13900 | MPa | ASTM D-790 |
| 拉伸模量 (3.2mm(0.125in),23℃(73℉)) | 10500 | MPa | ASTM D-638 |
| IZOD冲击强度 (3.2mm(0.126in)) | 160 | J/m | ASTM D-256 |
| 弯曲强度 (0.8mm(0.032in),23℃(73℉)) | 158 | MPa | ASTM D-790 |
| 拉伸强度 (3.2mm(0.125in),23℃(73℉)) | 125 | MPa | ASTM D-638 |
| 损耗因数 | ASTM D-2520 B | ||
| (0.8mm(0.032in),23℃(73℉)) | 0.001 | ||
| (1.6mm(0.063in),23℃(73℉)) | 0.002 | ||
| 介电强度 (0.8mm) | 49 | Kv/mm | ASTM D-149 |
| 介电常数 | |||
| (0.8mm(0.032in),23℃(73℉)) | 3.9 | ASTM D-2520 B | |
| (0.8mm(0.032in)) | 2.9 | ASTM D-150 | |
| (1.6mm(0.063in),23℃(73℉)) | 4 | ASTM D-2520 B | |
| 损耗因数 (0.8mm(0.032in)) | 0.013 | ASTM D-150 | |
| 介电强度 (3.2mm) | 26 | Kv/mm | ASTM D-149 |
| 介电常数 | |||
| (0.8mm) | 3.3 | ASTM D-150 | |
| (3.2mm(0.125in),23℃(73℉)) | 4.1 | ASTM D-2520 B | |
| (3.2mm(0.125in)) | 3.6 | ASTM D-150 | |
| 介电强度 (1.6mm) | 41 | Kv/mm | ASTM D-149 |
| 损耗因数 (1.6mm(0.063in),23℃(73℉)) | 0.001 | ASTM D-2520 B | |
| 介电常数 (3.2mm(0.125in)) | 3.6 | ASTM D-150 | |
| 损耗因数 | ASTM D-150 | ||
| (0.8mm(0.032in)) | 0.029 | ||
| (0.8mm(0.032in)) | 0.009 | ||
| (3.2mm(0.125in)) | 0.013 | ||
| 介电常数 (0.8mm(0.032in)) | 3.3 | ASTM D-150 | |
| 表面电阻率 | >1×10 | Ohm | ASTM D-257 |
| 介电常数 | ASTM D-2520 B |
| 介电常数 | ASTM D-2520 B | ||
| (3.2mm(0.125in),23℃(73℉)) | 3.9 | ||
| (0.8mm(0.032in),23℃(73℉)) | 4.1 | ||
| 体积电阻率 | >1×10 | Ohm-cm | ASTM D-257 |
| 损耗因数 | ASTM D-2520 B | ||
| (0.8mm(0.032in),23℃(73℉)) | 0.002 | ||
| (3.2mm(0.125in),23℃(73℉)) | 0.002 | ||
| (3.2mm(0.125in),23℃(73℉)) | 0.001 | ||
| 介电常数 | |||
| (3.2mm(0.125in)) | 3.2 | ASTM D-150 | |
| (1.6mm(0.063in),23℃(73℉)) | 3.9 | ASTM D-2520 B | |
| 损耗因数 | ASTM D-150 | ||
| (3.2mm(0.125in)) | 0.028 |
| (3.2mm(0.125in)) | 0.008 |
| 热变形温度 (1.80MPa) | 239 | ℃ | ASTM D-648 |
| 玻璃化转变温度 | 120 | ℃ | ASTM D-3418 |
| 模压温度范围 | 30-95 | ℃ | |
| 干燥温度 | 135 | ℃ | |
| 熔点 | 335 | ℃ | ASTM D-3418 |
| 解链温度范围 | 350-360 | ℃ |
| 工业含水量 | <0.01 | % | |
| RTI,Electrical (1.5mm) | 130 | ℃ | UL 746-B |
| RTI,Mechanical with Impact (1.5mm) | 130 | ℃ | UL 746-B |
| RTI,Mechanical without Impact (1.5mm) | 130 | ℃ | UL 746-B |
其他新闻
- 现货 LCP 美国杜邦 6130LX-BK010 玻纤增强 注塑级 液晶聚合物 2024-05-21
- 现货销售 美国杜邦 LCP 6130 阻燃V0 加纤30% 连接器应用 2024-05-21
- 高流动 LCP 美国塞拉尼斯 H145 玻纤增强 阻燃级 复杂零件应用 2024-05-21
- 低翘曲 美国塞拉尼斯 LCP FIT30 高流动 阻燃V0 矿物填充材料 2024-05-21
- 低翘曲 LCP 美国塞拉尼斯 E540I VD3071 高流动 矿物填充40% 2024-05-21
- 高流动 LCP 美国塞拉尼斯 E130i-VC3030-GY 耐水解 阻燃 电子电气应用 2024-05-21
- 供应 LCP 美国塞拉尼斯 A430D-BK 防火阻燃 注塑级 液晶聚合物 2024-05-21
- 现货 LCP 美国塞拉尼斯 E471iVF2201高强度 抗冲击 电子接插件应用 2024-05-21
- 供应 LCP 美国塞拉尼斯 ZEM 5000 低翘曲 阻燃 玻纤增强 连接器应用 2024-05-21
- 现货 LCP 美国塞拉尼斯 ZE55205 BK 阻燃V0 高介电常数 2024-05-21
- 50%矿物填充 LCP 美国塞拉尼斯 ZE55201阻燃V0 优异的平面度 2024-05-21
- 抗化学 LCP 美国塞拉尼斯 V400P 高清晰度 阻隔树脂 薄膜应用 2024-05-21
- 供应 LCP 美国塞拉尼斯 V143XL-BLACK 防火阻燃 耐高温 玻纤增强 2024-05-21
- 阻燃级 LCP 美国塞拉尼斯 S540 高流动 低翘曲 矿物填充40% 2024-05-21
- 高流动 LCP 美国塞拉尼斯 MT1300 阻燃 生物兼容性 医疗领域应用 2024-05-21
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com
产品分类
站内搜索