PC 基础创新塑料(美国) 4019 增强级 高刚性 成型快 易流动
LEXAN™ EXL4019 resin
Polycarbonate
SABIC Innovative Plastics
9.0% 玻璃纤维增强材料
产品说明：
LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only.
物性信息：
| 填料/增强材料 |
|
| 特性 |
|
| 外观 |
|
| 加工方法 |
|
| 比重 | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 7.5 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 6.50 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.20 到 0.60 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.20 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.15 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.40 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 3950 | MPa | ASTM D638 |
| -- | 3900 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 55.0 | MPa | ASTM D638 |
| 屈服 | 54.0 | MPa | ISO 527-2/5 |
| 断裂 3 | 45.0 | MPa | ASTM D638 |
| 断裂 | 48.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服 4 | 4.3 | % | ASTM D638 |
| 屈服 | 4.3 | % | ISO 527-2/5 |
| 断裂 5 | 14 | % | ASTM D638 |
| 断裂 | 8.7 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距 6 | 3500 | MPa | ASTM D790 |
| -- 7 | 3450 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 98.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 103 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 25 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 10 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 350 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 25 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 13 | ISO 180/1U | ||
| -30°C | 无断裂 | ISO 180/1U | |
| 23°C | 无断裂 | ISO 180/1U | |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距 14 | 135 | °C | ISO 75-2/Ae |
| 维卡软化温度 | 146 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 15 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| 线形热膨胀系数 | ASTM E831, ISO 11359-2 | ||
| 流动 : -40 到 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
其他新闻
- 注塑级 PC 基础创新塑料 3414R-131 玻纤增强40% 脱模 2024-11-17
- 脱模级PC 基础创新塑料(美国) 244R 中等粘性 阻燃 食品接触的合规性 2024-11-17
- 高抗冲 PC 基础创新塑料 241-111 阻燃 注塑成型 2024-11-17
- 注塑级PC 基础创新塑料(美国) 201R-701 阻燃V0 聚碳酸酯 2024-11-17
- 注塑级PC 基础创新塑料(美国)101-111耐高温 玻纤增强 2024-11-17
- 阻燃级 PC 基础创新塑料 LUX9610 透明 光学性 灯具照明 2024-11-17
- PC 基础创新塑料 LUX2114G-WH8B491高流动 抗UV 电子/电器应用 2024-11-17
- PC 基础创新塑料 LUX2114 透明级抗紫外线 脱模 2024-11-17
- PC 基础创新塑料 HFD4413-BK1E711玻纤增强30% 高流动 2024-11-17
- 增强级PC 基础创新塑料 HFD4271 BK1G100L 冲击改性 高流动 2024-11-17
- 高流动PC 基础创新塑料 HFD1830 NA9E109T 抗紫外线 2024-11-17
- PC基础创新塑料(南沙) HFD1810 高流动 延展性共聚物 2024-11-17
- PC 基础创新塑料 HF1140-111FC 尺寸稳定 中等粘度 食品级 2024-11-17
- PC 基础创新塑料 FXD171R 8A8D016X 注塑级 灯具照明应用 2024-11-17
- 易流动 PC 基础创新塑料 EXL9414T-NA9G003T 抗冲击 阻燃 2024-11-17
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com
产品分类
站内搜索