Polycarbonate
SABIC Innovative Plastics
产品说明：
LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
物性信息：
| 特性 | 共聚物 可加工性，良好 快的成型周期 流动性中等 通用 脱模性能良好 延展性 |
| 用途 | 通用 |
| 外观 | 不透明 可用颜色 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.40 到 0.80 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.40 到 0.80 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.35 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.15 | % | ISO 62 |
| 洛氏硬度 | ASTM D785 | ||
| L 计秤 | 89 | ASTM D785 | |
| R 级 | 121 | ASTM D785 |
| 拉伸模量 | |||
| -- 1 | 2020 | MPa | ASTM D638 |
| -- | 2150 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 55.5 | MPa | ASTM D638 |
| 屈服 | 57.0 | MPa | ISO 527-2/50 |
| 断裂 3 | 50.3 | MPa | ASTM D638 |
| 断裂 | 60.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 4 | 6.0 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/50 |
| 断裂 5 | 98 | % | ASTM D638 |
| 断裂 | 120 | % | ISO 527-2/50 |
| 50.0 mm 跨距 6 | 2230 | MPa | ASTM D790 |
| -- 7 | 2250 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 85.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 92.4 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 9 | ISO 179/1eA | ||
| -30°C | 65 | kJ/m² | ISO 179/1eA |
| 23°C | 70 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 10 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 770 | J/m | ASTM D256 |
| 23°C | 870 | J/m | ASTM D256 |
| -30°C 11 | 60 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 13 | ISO 180/1U | ||
| -30°C | 无断裂 | ISO 180/1U | |
| 23°C | 无断裂 | ISO 180/1U | |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 100 mm 跨距 14 | 140 | °C | ISO 75-2/Be |
| 1.8 MPa, 未退火, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距 15 | 128 | °C | ISO 75-2/Ae |
| 维卡软化温度 | |||
| -- | 145 | °C | ASTM D1525, ISO 306/B50 11 16 |
| -- | 146 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
- 基础创新塑料PC 940A-116 阻燃 中等粘性 电气/电子领域应用 2024-05-21
- PC 基础创新塑料 945-701无卤阻燃 通用级聚碳酸酯 2024-05-21
- 无卤阻燃 PC 基础创新塑料(南沙) 945A-116 注塑级防弹胶 2024-05-21
- 聚碳酸酯的成型工艺 2024-05-21
- PC的制品成型方法 2024-05-21
- 聚碳酸酯的性能与特征 2024-05-21
- PC塑料的成型工艺 2024-05-21
- 聚碳酸酯的改性用途 2024-05-21
- PC塑料的用途 2024-05-21
- PC塑料的主要优点 2024-05-21
- PC塑料的物理性质 2024-05-21
- 聚碳酸酯的化学性质 2024-05-21
- 什么是聚碳酸酯 2024-05-21
- 玻纤增强 阻燃 FR82G33 V1 BKB523 美国杜邦 PA66 机械连接器 2024-05-21
- PA66 美国杜邦HTN501 NC010 高强度 阻燃 电子电器部件 2024-05-21
联系方式
- 地址：深圳市龙华区观湖街道樟溪社区下围工业区一路 6 号智谷 C1 栋 213A
- 电话：0755-21047619
- 销售经理：刘春梅
- 手机：18819106372
- 传真：暂无
- 微信：18819106372
- QQ：241813087
- Email：241813087@qq.com