可电镀 PC/ABS 基础创新塑料 NX10302 激光打标 电子显示器应用
可电镀 PC/ABS 基础创新塑料 NX10302 激光打标 电子显示器应用
Polycarbonate + ABS
SABIC Innovative Plastics Asia Pacific
产品说明：
This is a PC/ABS compound with improved plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
物性信息：
| 黄卡编号 | E207780-101343771 |
| 特性 | 可电镀 |
| 加工方法 | 注射成型 |
| 比重 | 1.26 | g/cm³ | ASTM D792 |
| 溶化体积流率（MVR） (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| 收缩率 | ASTM D955 | ||
| 流动 : 24小时 | 0.60 到 0.65 | % | ASTM D955 |
| 横向流动 : 24小时 | 0.50 到 0.56 | % | ASTM D955 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.010 | % | ASTM D570 |
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| 拉伸模量 1 | 2480 | MPa | ASTM D638 |
| 抗张强度 2 | ASTM D638 | ||
| 屈服 | 46.0 | MPa | ASTM D638 |
| 断裂 | 47.0 | MPa | ASTM D638 |
| 伸长率 3 | ASTM D638 | ||
| 屈服 | 4.2 | % | ASTM D638 |
| 断裂 | 100 | % | ASTM D638 |
| 弯曲模量 4(50.0 mm 跨距) | 2400 | MPa | ASTM D790 |
| 弯曲强度 5 | ASTM D790 | ||
| 屈服, 50.0 mm 跨距 | 80.0 | MPa | ASTM D790 |
| 断裂, 50.0 mm 跨距 | 79.0 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C) | 600 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 无断裂 | ASTM D4812 |
| 载荷下热变形温度 (1.8 MPa, 未退火, 3.20 mm) | 108 | °C | ASTM D648 |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 : -40 到 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| 横向 : -40 到 40°C | 9.1E-5 | cm/cm/°C | ASTM E831 |
| 相对电容率 (1.00 GHz) | 2.74 | IEC 60250 | |
| 耗散因数 (1.00 GHz) | 3.0E-3 | IEC 60250 |
| 干燥温度 | 85.0 到 100 | °C | |
| 干燥时间 | 6.0 到 8.0 | hr | |
| 料筒后部温度 | 250 到 270 | °C | |
| 料筒中部温度 | 250 到 270 | °C | |
| 料筒前部温度 | 250 到 280 | °C | |
| 射嘴温度 | 250 到 290 | °C | |
| 加工（熔体）温度 | 250 到 290 | °C | |
| 模具温度 | 60.0 到 90.0 | °C | |
| 背压 | 0.300 到 0.700 | MPa | |
| 螺杆转速 | 40 到 70 | rpm |