高抗冲 PC/ABS 基础创新塑料(上海) CX7240U 无卤阻燃 易流动 抗UV 薄壁部件
高抗冲 PC/ABS 基础创新塑料(上海) CX7240U 无卤阻燃 易流动 抗UV 薄壁部件
Polycarbonate + ABS
SABIC Innovative Plastics
产品说明：
CYCOLOY CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistance. Excellent flow and impact balance together with the thin wall flame resistance and all color options make CYCOLOY CX7240U an ideal candidate for a wide variety of thin wall applications.
物性信息：
| 黄卡编号 | E121562-642976 |
| 添加剂 | 紫外线稳定剂 阻燃性 |
| 特性 | Chlorine Free 抗撞击性，良好 良好的流动性 无溴 阻燃性 |
| 用途 | 薄壁部件 |
| 加工方法 | 注射成型 |
| 比重 | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| 收缩率 - 流动 (3.20 mm) | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.20 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.10 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 2950 | MPa | ASTM D638 |
| -- | 2530 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 65.0 | MPa | ASTM D638 |
| 屈服 | 65.0 | MPa | ISO 527-2/50 |
| 断裂 3 | 58.0 | MPa | ASTM D638 |
| 断裂 | 50.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 4 | 4.1 | % | ASTM D638 |
| 屈服 | 4.0 | % | ISO 527-2/50 |
| 断裂 5 | 100 | % | ASTM D638 |
| 断裂 | 90 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 6 | 2750 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 96.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 104 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 500 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 20 | kJ/m² | ISO 180/1A |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火, 3.20 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 12 | 93.0 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 106 | °C | ASTM D1525 13 |
| -- | 110 | °C | ISO 306/B50 |
| -- | 113 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动 : -40 到 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| 流动 : -40 到 40°C | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 : -40 到 40°C | 5.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |