高抗冲 PCTG 美国伊士曼 0603 耐化学 外观优良 注塑 挤出吹塑成型
Copolyester
Eastman Chemical Company
产品说明:
Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying re of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment.
Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future.
*DRYSTAR is only available in the Asia Pacific Region.
物性信息:
特性 | 抗撞击性,良好 耐化学性良好 外观良好 |
形式 | 粒子 |
加工方法 | 挤出吹塑成型 型材挤出成型 注射成型 |
比重 | 1.27 | g/cm³ | ASTM D792 |
收缩率 - 流动 (3.20 mm) | 0.20 到 0.50 | % | ASTM D955 |
拉伸模量 | |||
23°C | 2030 | MPa | ASTM D638 |
23°C | 2000 | MPa | ISO 527-2 |
抗张强度 | |||
屈服, 23°C | 50.0 | MPa | ASTM D638 |
屈服, 23°C | 48.0 | MPa | ISO 527-2 |
断裂, 23°C | 30.0 | MPa | ASTM D638 |
断裂, 23°C | 29.0 | MPa | ISO 527-2 |
伸长率 | |||
屈服, 23°C | 4.4 | % | ASTM D638 |
屈服, 23°C | 4.0 | % | ISO 527-2 |
断裂, 23°C | 180 | % | ASTM D638 |
断裂, 23°C | 200 | % | ISO 527-2 |
弯曲模量 | |||
23°C | 2060 | MPa | ASTM D790 |
23°C | 2100 | MPa | ISO 178 |
弯曲强度 | |||
23°C | 68.0 | MPa | ASTM D790 |
23°C | 67.0 | MPa | ISO 178 |
悬壁梁缺口冲击强度 | |||
-40°C | 40 | J/m | ASTM D256 |
23°C | 110 | J/m | ASTM D256 |
-40°C | 4.4 | kJ/m² | ISO 180 |
23°C | 9.4 | kJ/m² | ISO 180 |
无缺口悬臂梁冲击 | ASTM D4812 | ||
-40°C | 无断裂 | ASTM D4812 | |
23°C | 无断裂 | ASTM D4812 |
载荷下热变形温度 | |||
0.45 MPa, 未退火 | 70.0 | °C | ASTM D648, ISO 75-2/B |
1.8 MPa, 未退火 | 62.0 | °C | ASTM D648, ISO 75-2/A |
透射率 | 90.0 | % | ASTM D1003 |
雾度 | 0.20 | % | ASTM D1003 |
干燥温度 | 71.0 | °C | |
干燥时间 | 6.0 | hr | |
加工(熔体)温度 | 249 到 271 | °C | |
模具温度 | 16.0 到 38.0 | °C |