高流动 PCTG 美国伊士曼 TX1501HF低粘度 脱模 消费品应用领域

Tritan™ TX1501HF

Copolyester

Eastman Chemical Company

产品说明：

Eastman Tritan™ copolyester TX1501HF is a high flow grade of Eastman Tritan™. Eastman Tritan™ copolyester TX1501HF has viscosity reductions of 40-50% relative to Eastman Tritan™ copolyester TX1001. Eastman Tritan™ copolyester TX1501HF contains a mold release derived from vegetable based sources. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan™ copolyester TX1501HF may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan™ copolyester TX1501HF is certified to NSF/ANSI Standard 51 for Food E Materials and is also certified to NSF/ANSI Standard 61 - Drinking Water System Components-Health Effects.

物性信息：

基本信息

黄卡编号	E118289-100238009
添加剂	脱模
特性	低粘度 抗撞击性，高 可加工性，良好 快的成型周期 流动性高 耐化学性良好 耐热性，高 耐用性 清晰度，高 韧性良好 食品接触的合规性 水解稳定 脱模性能良好 无定形的
用途	电器用具 家用货品 消费品应用领域
机构评级	FDA 食品接触, 未评级 NSF 51 NSF 61
加工方法	注射成型

物理性能额定值单位制测试方法

比重	1.18	g/cm³	ASTM D792
收缩率 - 流动	0.50 到 0.70	%	ASTM D955

硬度额定值单位制测试方法

洛氏硬度 (R 级, 23°C)	111		ASTM D785

机械性能额定值单位制测试方法

拉伸模量
23°C	1580	MPa	ASTM D638
23°C	1600	MPa	ISO 527-2
抗张强度
屈服, 23°C	43.0	MPa	ASTM D638
屈服, 23°C	44.0	MPa	ISO 527-2
断裂, 23°C	52.0	MPa	ASTM D638
断裂, 23°C	49.0	MPa	ISO 527-2
伸长率
屈服, 23°C	7.0	%	ASTM D638, ISO 527-2
断裂, 23°C	210	%	ASTM D638
断裂, 23°C	150	%	ISO 527-2
弯曲模量
23°C	1580	MPa	ASTM D790
23°C	1500	MPa	ISO 178
弯曲应力
23°C	60.0	MPa	ISO 178
屈服, 23°C	64.0	MPa	ASTM D790

冲击性能额定值单位制测试方法

悬壁梁缺口冲击强度
23°C	860	J/m	ASTM D256
-40°C	11	kJ/m²	ISO 180
23°C	83	kJ/m²	ISO 180
无缺口悬臂梁冲击 (23°C)	无断裂		ASTM D4812

热性能额定值单位制测试方法

载荷下热变形温度			ASTM D648
0.45 MPa, 未退火	94.0	°C	ASTM D648
1.8 MPa, 未退火	81.0	°C	ASTM D648

光学性能额定值单位制测试方法

透射率 (总计)	91.0	%	ASTM D1003
雾度	< 1.0	%	ASTM D1003

注射额定值单位制

干燥温度	88.0	°C
干燥时间	4.0 到 6.0	hr
加工（熔体）温度	260 到 282	°C
模具温度	38.0 到 66.0	°