矿物填充 735-BK1066 基础创新塑料(美国) PBT 低收缩 家电部件 电动加热器
VALOX™ 735 resin
Polybutylene Terephthalate
SABIC Innovative Plastics
40% 玻璃矿物
产品说明:
40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
物性信息:
黄卡编号 | E121562-220805 |
填料/增强材料 | 玻璃\矿物, 40% 填料按重量 |
特性 | 收缩性低 |
用途 | 家电部件 |
外观 | 黑色 自然色 |
加工方法 | 注射成型 |
多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) |
比重 | 1.62 | g/cm³ | ASTM D792 |
特定体积 | 0.621 | cm³/g | ASTM D792 |
收缩率 | 内部方法 | ||
流动 1 | 0.30 到 0.40 | % | 内部方法 |
流动 2 | 0.40 到 0.60 | % | 内部方法 |
横向流动 3 | 0.40 到 0.60 | % | 内部方法 |
横向流动 4 | 0.60 到 0.80 | % | 内部方法 |
吸水率 (24 hr) | 0.070 | % | ASTM D570 |
洛氏硬度 (R 级) | 109 | ASTM D785 |
抗张强度 5(断裂) | 75.8 | MPa | ASTM D638 |
弯曲模量 6(50.0 mm 跨距) | 8270 | MPa | ASTM D790 |
弯曲强度 7(断裂, 50.0 mm 跨距) | 124 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (23°C) | 75 | J/m | ASTM D256 |
无缺口悬臂梁冲击 (23°C) | 430 | J/m | ASTM D4812 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火, 6.40 mm | 216 | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | 199 | °C | ASTM D648 |
线形热膨胀系数 - 流动 | ASTM E831 | ||
-40 到 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
60 到 138°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
RTI Elec | 140 | °C | UL 746 |
RTI Imp | 140 | °C | UL 746 |
RTI | 140 | °C | UL 746 |
体积电阻率 | 1.3E+15 | ohms·cm | ASTM D257 |
介电强度 | ASTM D149 | ||
1.60 mm, in Oil | 30 | kV/mm | ASTM D149 |
3.20 mm, in Air | 24 | kV/mm | ASTM D149 |
介电常数 | ASTM D150 | ||
100 Hz | 4.30 | ASTM D150 | |
1 MHz | 4.00 | ASTM D150 | |
耗散因数 | ASTM D150 | ||
100 Hz | 1.0E-3 | ASTM D150 | |
1 MHz | 0.020 | ASTM D150 | |
耐电弧性 8 | PLC 6 | ASTM D495 | |
相比耐漏电起痕指数(CTI) | PLC 2 | UL 746 | |
高电弧燃烧指数(HAI) | PLC 3 | UL 746 | |
高电压电弧起痕速率 (HVTR) | PLC 1 | UL 746 | |
热丝引燃 (HWI) | PLC 0 | UL 746 |
矿物填充 735-BK1066 基础创新塑料(美国) PBT 低收缩 家电部件 电动加热器