可喷涂 PPA 美国索尔维 5950HFFR BK000 高流动 阻燃 电镀级 薄壁部件

Kalix® 5950 HFFR

High Performance Polyamide

Solvay Specialty Polymers

50% 玻璃纤维增强材料

产品说明：

Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry.

Black: Kalix® 5950 BK 000 HFFR

White: Kalix® 5950 WH 000 HFFR

物性信息：

基本信息

黄卡编号	E95746-101619491
填料/增强材料	玻璃纤维增强材料, 50% 填料按重量
特性	尺寸稳定性良好 低翘曲性 低吸湿性 刚性，高 高强度 抗撞击性，良好 可电镀 可喷涂的 流动性高 无卤 优良外观 阻燃性
用途	薄壁部件 电气/电子应用领域 电气元件 手机
RoHS 合规性	RoHS 合规
外观	白色 黑色
形式	粒子
加工方法	注射成型
部件标识代码 (ISO 11469)	>PAX6/MXD6-GF50

物理性能额定值单位制测试方法

密度	1.68	g/cm³	ISO 1183
收缩率 1			内部方法
垂直流动方向	0.18	%	内部方法
流动方向	0.060	%	内部方法
吸水率 (23°C, 24 hr)	0.11	%	ISO 62

机械性能额定值单位制测试方法

拉伸模量	20000	MPa	ISO 527-2
拉伸应力 (屈服)	245	MPa	ISO 527-2
拉伸应变 (断裂)	1.8	%	ISO 527-2
弯曲模量	19000	MPa	ISO 178
弯曲应力	350	MPa	ISO 178
断裂弯曲应变	2.2	%	ISO 178
抗张强度 - 50% RH，平衡	183	MPa	ISO 527-2
拉伸断裂应变 - 50% RH，平衡	1.7	%	ISO 527-2
拉伸模量 - 50% RH，平衡	19.7	GPa	ISO 527-2

冲击性能额定值单位制测试方法

悬壁梁缺口冲击强度	15	kJ/m²	ISO 180/1A
无缺口伊佐德冲击强度	50	kJ/m²	ISO 180

热性能额定值单位制测试方法

热变形温度
0.45 MPa, 未退火	255	°C	ISO 75-2/B
1.8 MPa, 未退火	247	°C	ISO 75-2/A
玻璃转化温度	40.0	°C	ASTM D3418

电气性能额定值
测试方法

介电常数 2(2.40 GHz)	4.48		ASTM D2520
耗散因数 3(2.40 GHz)	0.011		ASTM D2520

可燃性额定值
测试方法

UL 阻燃等级			UL 94
0.400 mm, 所有颜色	V-0		UL 94
1.50 mm, 所有颜色	5VA		UL 94

可喷涂 PPA 美国索尔维 5950HFFR BK000 高流动 阻燃 电镀级 薄壁部件