非卤化WCD835 BK1006 基础创新塑料(美国)PPO 低气味 柔韧性 电缆护套
观看非卤化WCD835 BK1006 基础创新塑料(美国)PPO 低气味 柔韧性 电缆护套视频:
非卤化WCD835 BK1006 基础创新塑料(美国)PPO 低气味 柔韧性 电缆护套
Polyphenylene Ether + TPE
SABIC Innovative Plastics
产品说明:
Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 re 80C end use temperature rating and good heat deformation performance as defined by UL 1581. 83 Shore A hardness. Processing typically conducted on standard extrusion e UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.
物性信息:
特性 | 良好的柔韧性 气味低到无 无卤 |
用途 | 电线电缆应用 电线护套 |
加工方法 | 挤出涂层 |
比重 | 1.04 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (250°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238 |
肖氏硬度 (邵氏 A, 30 秒) | 83 | ASTM D2240 |
抗张强度 | |||
断裂 | 17.0 | MPa | UL 1581 |
断裂 1 | 10.0 | MPa | ASTM D638 |
断裂, 113°C 2 | 18.0 | MPa | UL 1581 |
断裂 | 10.0 | MPa | ISO 527-2/50 |
伸长率 | |||
断裂 | 270 | % | UL 1581 |
断裂 3 | 250 | % | ASTM D638 |
断裂, 113°C 4 | 250 | % | UL 1581 |
断裂 | 230 | % | ISO 527-2/50 |
弯曲模量 5 | |||
100 mm 跨距 | 40.0 | MPa | ASTM D790 |
-- | 35.0 | MPa | ISO 178 |
脆化温度 | < -40.0 | °C | ASTM D746 |
UL温度额定值 | 80 | °C | UL 1581 |
Heat Deformation 6(100°C) | 20 | % | UL 1581 |
VW-1 | Pass | UL 1581 |
体积电阻率 | 9.0E+15 | ohms·cm | IEC 60093 |
漏电起痕指数 | 600 | V | IEC 60112 |
灼热丝易燃指数 (3.00 mm) | 850 | °C | IEC 60695-2-12 |
热灯丝点火温度 (3.00 mm) | 750 | °C | IEC 60695-2-13 |
干燥温度 | 75.0 到 85.0 | °C | |
干燥时间 | 5.0 到 7.0 | hr | |
建议的Zui大水分含量 | 0.020 | % | |
料筒1区温度 | 180 到 220 | °C | |
料筒3区温度 | 220 到 250 | °C | |
料筒5区温度 | 220 到 250 | °C | |
熔体温度 | 220 到 250 | °C | |
口模温度 | 220 到 250 | °C |
非卤化WCD835 BK1006 基础创新塑料(美国)PPO 低气味 柔韧性 电缆护套
展开全文