注塑级 PEEK 德国赢创德固赛 2000CF30 碳纤增强30% 耐化学聚醚醚酮

VESTAKEEP® 2000 CF30

Polyetheretherketone

Evonik Industries AG

30% 碳纤维增强材料

产品说明：

Carbon fiber-reinforced (30%) polyether ether ketone

VESTAKEEP 2000 CF30 is a medium-viscosity, carbon fiber-reinforced (30%) polyether ether ketone for injection molding.

The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 CF30 are self-extinguishing.

VESTAKEEP 2000 CF30 can be processed by common injection molding machines for thermoplastics.

We recommend a melt temperature between 380°C and 400°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C.

物性信息：

基本信息

填料/增强材料	碳纤维增强材料, 30% 填料按重量
特性	半结晶 耐化学性良好 中等粘性 自熄
形式	颗粒
加工方法	注射成型

物理性能额定值单位制测试方法

密度	1.38	g/cm³	ISO 1183
溶化体积流率（MVR） (380°C/5.0 kg)	10.0	cm³/10min	ISO 1133
收缩率 1			ISO 294-4
垂直流动方向 : 180°C, 2.00 mm	0.40	%	ISO 294-4
流动方向 : 180°C, 2.00 mm	0.0	%	ISO 294-4

机械性能额定值单位制测试方法

拉伸模量	23000	MPa	ISO 527-2
拉伸应力 (断裂)	240	MPa	ISO 527-2
拉伸应变 (断裂)	2.0	%	ISO 527-2

冲击性能额定值单位制测试方法

简支梁缺口冲击强度			ISO 179/1eA
-30°C, 完全断裂	8.0	kJ/m²	ISO 179/1eA
23°C, 完全断裂	9.0	kJ/m²	ISO 179/1eA
简支梁无缺口冲击强度			ISO 179/1eU
-30°C, 完全断裂	45	kJ/m²	ISO 179/1eU
23°C, 完全断裂	45	kJ/m²	ISO 179/1eU

热性能额定值单位制测试方法

热变形温度
0.45 MPa, 未退火	340	°C	ISO 75-2/B
1.8 MPa, 未退火	330	°C	ISO 75-2/A
维卡软化温度
--	343	°C	ISO 306/A
--	340	°C	ISO 306/B
熔融温度 2	340	°C	ISO 11357-3
线形热膨胀系数 - 流动 (23 到 55°C)	1.0E-5	cm/cm/°C	ISO 11359-2

电气性能额定值单位制测试方法

表面电阻率	1.0E+5	ohms	IEC 60093
体积电阻率	1.0E+6	ohms·cm	IEC 60093

可燃性额定值单位制测试方法

UL 阻燃等级 (1.60 mm)	V-0		UL 94
灼热丝易燃指数 (2.00 mm)	960	°C	IEC 60695-2-12
热灯丝点火温度 (2.00 mm)	875	°C	IEC 60695-2-13