加纤15% PEEK 美国索尔维 KT-880 GF15 高刚性 抗伽马辐射 航空航天领域

KetaSpire® KT-880 GF15

Polyetheretherketone

Solvay Specialty Polymers

15% 玻璃纤维增强材料

产品说明：

KetaSpire® KT-880 GF15 is a high flow, 15% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. The low fiberglass loading gives the resin improved surface aesthetics and reduced anisotropy over comparable 30% glass reinforced formulations.

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.

These properties make it well-suited for applications in oil & gas, healthcare, transportation, electronics, chemical processing and other industrial uses.

Natural: KT-880 GF15 NT

物性信息：

基本信息

填料/增强材料	玻璃纤维增强材料, 15% 填料按重量
特性	尺寸稳定性良好 电子束消毒 放射性可透的 辐射消毒 刚性，高 高强度 高压锅消毒 好的消毒性 环氧乙烷消毒 抗伽马辐射 流动性高 耐化学性良好 耐疲劳性能 耐热性，高 耐蒸汽 热消毒 生物兼容性 用蒸汽消毒 阻燃性
用途	薄膜 泵件 电气/电子应用领域 飞机应用 工业应用 连接器 密封件 汽车领域的应用 石油/天然气用品 外科器械 牙齿应用领域 医疗/护理用品 医疗器材 医疗器械
RoHS 合规性	联系制造商
外观	棕黄色
形式	粒子
加工方法	注射成型

物理性能额定值单位制测试方法

比重	1.41	g/cm³	ASTM D792
灰份含量	15	%	ISO 3451-1

机械性能额定值单位制测试方法

弹性模量	6.61	GPa	ASTM D638
拉伸模量	6700	MPa	ASTM D638
拉伸应力 (断裂)	138	MPa	ASTM D638
拉伸应变 1(断裂)	5.0	%	ASTM D638
弯曲应力	231	MPa	ASTM D638

冲击性能额定值单位制测试方法

简支梁无缺口冲击强度	53	kJ/m²	ISO 179
悬壁梁缺口冲击强度
--	47	J/m	ASTM D256
--	5.0	kJ/m²	ISO 180
无缺口悬臂梁冲击	660	J/m	ASTM D256

热性能额定值单位制测试方法

热变形温度 (1.8 MPa, 未退火)	278	°C	ASTM D648

注射额定值单位制

干燥温度	150	°C
干燥时间	4.0	hr
料筒后部温度	365	°C
料筒中部温度	371	°C
料筒前部温度	377	°C
射嘴温度	382	°C
模具温度	177 到 204	°C
注射速度	快速
螺杆压缩比	2.5:1.0 到 3.5:1.0

KT-880 GF15,美国索尔维peek,增强级PEEK,医疗级peek,聚醚醚酮