抗冲击 PC 基础创新塑料 DX14354X-WH9G545 易着色 电气/电子领域应用
观看抗冲击 PC 基础创新塑料 DX14354X-WH9G545 易着色 电气/电子领域应用视频：
抗冲击 PC 基础创新塑料 DX14354X-WH9G545 易着色 电气/电子领域应用
Polycarbonate
SABIC Innovative Plastics Asia Pacific
产品说明：
LNP Thermocomp compound DX14354X is an improved flow, colorable compound based on PC copolymer resin developed for applications that require Laser Direct Structuring (LDS) for antenna, or electronic circuit manufacturing. Thermocomp compound DX14354X helps customers to improve productivity with stable plating and RF performance, excellent impact strength and surface finish.
物性信息：
| 黄卡编号 | E207780-102180157 |
| 特性 | 共聚物 抗撞击性，高 良好的着色性 优良外观 |
| 用途 | Laser Direct Structuring 电气/电子应用领域 |
| 加工方法 | 注射成型 |
| 密度 | 1.29 | g/cm³ | ASTM D792 |
| 溶化体积流率（MVR） | ISO 1133 | ||
| 260°C/5.0 kg | 25.0 | cm³/10min | ISO 1133 |
| 280°C/2.16 kg | 27.0 | cm³/10min | ISO 1133 |
| 280°C/21.6 kg | 22.0 | cm³/10min | ISO 1133 |
| 收缩率 | ASTM D955 | ||
| 流动 : 24小时 | 0.50 到 0.70 | % | ASTM D955 |
| 横向流动 : 24小时 | 0.50 到 0.70 | % | ASTM D955 |
| 吸水率 (平衡, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 2500 | MPa | ASTM D638 |
| -- | 2460 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 54.0 | MPa | ASTM D638 |
| 屈服 | 54.0 | MPa | ISO 527-2/50 |
| 断裂 3 | 49.0 | MPa | ASTM D638 |
| 断裂 | 47.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 4 | 5.0 | % | ASTM D638 |
| 屈服 | 5.0 | % | ISO 527-2/50 |
| 断裂 5 | 70 | % | ASTM D638 |
| 断裂 | 80 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2560 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 86.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 85.0 | MPa | ASTM D790 |
| 断裂, 50.0 mm 跨距 9 | 83.0 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | |||
| 23°C | 750 | J/m | ASTM D256 |
| 23°C 10 | 60 | kJ/m² | ISO 180/1A |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 111 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 11 | 113 | °C | ISO 75-2/Af |
| 维卡软化温度 | 128 | °C | ASTM D1525 12 |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 : -40 到 40°C | 5.7E-5 | cm/cm/°C | ASTM E831 |
| 横向 : -40 到 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| 表面电阻率 | 1.2E+16 | ohms | ASTM D257 |
| 体积电阻率 | 1.2E+16 | ohms·cm | ASTM D257 |
| 介电常数 | |||
| 1.00 GHz | 3.10 | ASTM D150 | |
| 1.10 GHz | 3.06 | 内部方法 | |
| 1.90 GHz | 3.08 | 内部方法 | |
| 5.00 GHz | 3.08 | 内部方法 | |
| 耗散因数 | |||
| 1.00 GHz | 6.0E-3 | ASTM D150 | |
| 1.10 GHz | 6.3E-3 | 内部方法 | |
| 1.90 GHz | 6.1E-3 | 内部方法 | |
| 5.00 GHz | 5.9E-3 | 内部方法 |
| UL 阻燃等级 (1.00 mm) | V-1 | UL 94 |