挤出级粉末 Kynar 721 法国阿科玛 PVDF 低分子量 薄壁部件 薄膜原料
Kynar® 721
Polyvinylidene Fluoride
Arkema
产品说明：
KYNAR® 720 is a semi-crystalline low molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply a grade suitable for a variety of processing requirements and end-use applications.
KYNAR® 720 is recommended for fine extrusion operations such as monofilament and thin, flat, and blown film. It is also suitable for injection molding applications where very thin cross-sections for intricate design require excellent melt flow characteristics. KYNAR® 720 is also suggested for coextrusion of composite constructions and as a base for filled or alloyed KYNAR® compounds.
The powder form of this resin grade is available as KYNAR® 721 PVDF.
物性信息：
| 黄卡编号 | E54699-636461 |
| 特性 | 半结晶 低分子量 |
| 用途 | Blown Film 薄壁部件 薄膜 |
| 形式 | 粉状 |
| 加工方法 | 挤出 注射成型 |
| 比重 | 1.77 到 1.79 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） | 5.0 到 27 | g/10 min | ASTM D1238 |
| 肖氏硬度 (邵氏 D, 23°C) | 76 到 80 | ASTM D2240 |
| 抗张强度 | ASTM D638 | ||
| 屈服, 23°C | 44.8 到 55.2 | MPa | ASTM D638 |
| 断裂, 23°C | 34.5 到 55.2 | MPa | ASTM D638 |
| 伸长率 (断裂, 23°C) | 20 到 99.99 | % | ASTM D638 |
| 弯曲模量 (23°C) | 1380 到 2310 | MPa | ASTM D790 |
| 弯曲强度 (23°C) | 58.6 到 75.8 | MPa | ASTM D790 |
| 压缩强度 (23°C) | 68.9 到 103 | MPa | ASTM D695 |
| 熔融峰值温度 | 165 到 172 | °C | ASTM D3418 |
| 体积电阻率 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| 熔体粘度 (232°C, 100 sec^-1) | 600 到 1200 | Pa·s | ASTM D3835 |