导电级 PEI 基础创新塑料(美国) EX12310C BKNAT 高纯度 碳纤增强
Polyether Imide
SABIC Innovative Plastics Asia Pacific
10% 碳纤维增强材料
产品说明：
LNP STAT-KON EX12310C is an Electrical Conductive thermoplastic compound featuring Electrostatic Discharge (ESD) Safe performance based on a unique Ultra Clean Polyetherimide resin reinforced with 10% carbon fiber. This compound provides good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding applications in the Hard Disk Drive and Semiconductor Industry. A unique feature of this material is its low C18-C40 hydrocarbons and this compound is manufactured using the LNP Clean Compounding Solution (CCS) Technology.
EX12310C BKNAT物性信息：
| 黄卡编号 | E207780-101997197 |
| 填料/增强材料 | 碳纤维增强材料, 10% 填料按重量 |
| 特性 | 尺寸稳定性良好 纯净/高纯度 导电 刚性，良好 静电放电保护 |
| 加工方法 | 注射成型 |
| 密度 1 | 1.31 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (367°C/6.6 kg) | 31 | g/10 min | ASTM D1238 |
| 收缩率 | ASTM D955 | ||
| 流动 : 24小时 | 0.20 到 0.40 | % | ASTM D955 |
| 横向流动 : 24小时 | 0.50 到 0.70 | % | ASTM D955 |
| 拉伸模量 | |||
| -- 2 | 9170 | MPa | ASTM D638 |
| -- | 8980 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 断裂 3 | 158 | MPa | ASTM D638 |
| 断裂 | 156 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 断裂 4 | 2.4 | % | ASTM D638 |
| 断裂 | 2.3 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距 5 | 8140 | MPa | ASTM D790 |
| -- 6 | 8410 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 225 | MPa | ISO 178 |
| 断裂, 50.0 mm 跨距 7 | 224 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 8(23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 (23°C) | 32 | J/m | ASTM D256 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 6.40 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 9 | 201 | °C | ISO 75-2/Af |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 : 40 到 120°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| 横向 : 40 到 120°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| 表面电阻率 | 4.0E+5 | ohms | ASTM D257 |
| 体积电阻率 | 5.1E+5 | ohms·cm | ASTM D257 |
| UL 阻燃等级 (0.600 mm, Testing by SABIC) | V-0 | UL 94 |
| 干燥温度 | 150 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 干燥时间，*大 | 24 | hr | |
| 建议的*大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 330 到 380 | °C | |
| 料筒中部温度 | 340 到 380 | °C | |
| 料筒前部温度 | 345 到 380 | °C | |
| 射嘴温度 | 345 到 380 | °C | |
| 加工（熔体）温度 | 350 到 380 | °C | |
| 模具温度 | 135 到 165 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm |
EX12310C BKNAT，导电级 PEI ，沙伯基础pei,高刚性PEI
EX12310C BKNAT，导电级 PEI ，沙伯基础pei,高刚性PEI