阻燃级PA6T 日本三井化学 E630N 高刚性 抗化学 电气/电子部件

ARLEN™ E630N

Polyamide 6T

Mitsui Chemicals, Inc.

30% 玻璃纤维增强材料

产品说明：

ARLEN™ E630N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ E630N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating.

Features:

High dimensional stability

High melting point

High rigidity

Minimum water absorption

Good chemical and heat resistance

Flame retardant

Applications:

Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.

物性信息：

基本信息

填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
添加剂	阻燃性
特性	Good Heat Resistance High Dimensional Stability 刚性，高 耐化学性良好 吸水低或不吸水 阻燃性
用途	电气/电子应用领域 开关 连接器
加工方法	注射成型

物理性能额定值单位制测试方法

比重	1.58	g/cm³	ASTM D792
收缩率			ASTM D955
流动	0.20	%	ASTM D955
横向流动	0.80	%	ASTM D955
吸水率 (23°C, 24 hr, 65%r.h)	2.1	%	ASTM D570

硬度额定值单位制测试方法

洛氏硬度 (M 级)	100		ASTM D785

机械性能额定值单位制测试方法

抗张强度	210	MPa	ASTM D638
伸长率 (断裂)	6.0	%	ASTM D638
弯曲模量	12500	MPa	ASTM D790
弯曲强度	275	MPa	ASTM D790

冲击性能额定值单位制测试方法

悬壁梁缺口冲击强度	100	J/m	ASTM D256

热性能额定值单位制测试方法

载荷下热变形温度 (1.8 MPa, 未退火)	310	°C	ASTM D648
玻璃转化温度	95.0	°C
熔融温度	320	°C
线形热膨胀系数			ASTM E831
流动	1.6E-5	cm/cm/°C	ASTM E831
横向	6.8E-5	cm/cm/°C	ASTM E831

电气性能额定值单位制测试方法

体积电阻率	1.0E+15	ohms·cm	ASTM D257
介电强度	24	kV/mm	ASTM D149
介电常数 (1 MHz)	3.90		ASTM D150
耗散因数 (1 MHz)	0.013		ASTM D150

可燃性额定值单位制测试方法

UL 阻燃等级	V-0		UL 94