Polycarbonate
SABIC Innovative Plastics
产品说明：
Low viscosity injection moldable, flame retardant PC. Exceptional surface appearance. Clear, tints and opaque colors.
物性信息：
| 黄卡编号 | E121562-101677336 |
| 添加剂 | 阻燃性 |
| 特性 | 优良外观 阻燃性 |
| 外观 | 不透明 可用颜色 清晰/透明 |
| 加工方法 | 注射成型 |
| 多点数据 | Compressive Stress vs. Strain (ASTM D695) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) |
| 比重 | ASTM D792 | ||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ASTM D792 |
| 特定体积 | 0.835 | cm³/g | ASTM D792 |
| Radiant Panel Listing (UL) | YES |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 平衡, 100°C | 0.58 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 70 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 抗张强度 1 | ASTM D638 | ||
| 屈服 | 62.1 | MPa | ASTM D638 |
| 断裂 | 55.8 | MPa | ASTM D638 |
| 伸长率 2 | ASTM D638 | ||
| 屈服 | 7.0 | % | ASTM D638 |
| 断裂 | 90 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 2240 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 91.0 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| 悬壁梁缺口冲击强度 (23°C) | 640 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 3200 | J/m | ASTM D4812 |
| 落锤冲击 (23°C) | 169 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 525 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 132 | °C | ASTM D648 |
| 维卡软化温度 | 152 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-40 到 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 导热系数 | 0.19 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 17 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.01 | ASTM D150 | |
| 60 Hz | 3.01 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| 耐电弧性 7 | PLC 7 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 2 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 3 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 2 | UL 746 |
发布时间：2024-11-30
展开全文
其他新闻
- 高刚性PC 基础创新塑料(美国) EXL4419-739 中流动 玻纤增强材料 2024-11-30
- 脱模级PC 基础创新塑料(美国) 121R-21051非卤化 注塑成型 2024-11-30
- PC基础创新塑料 EXL1414T NA8A005T 中等流动 成型快 通用级 2024-11-30
- 阻燃级 PC 基础创新塑料 943 NC 抗UV 中等粘性 电气/电子部件 2024-11-30
- 耐低温 阻燃 PC 基础创新塑料1414 BK1A329 透明聚碳酸酯 2024-11-30
- PC 基础创新塑料 3412R-739 防火V0 加纤30% 黑色颗粒 2024-11-30
- 阻燃级 PC基础创新塑料(南沙) 943A-116 抗UV 中等粘性 外观优良 2024-11-30
- 阻燃级PC 基础创新塑料(南沙) 940-701 中等粘性 注塑成型 2024-11-30
- 高刚性 抗冲击 PC 基础创新塑料(南沙) 500R-739 阻燃 玻纤增强材料 2024-11-30
- 基础创新塑料(沙特)PC 1000R 抗紫外线 透明级 灯具照明 汽车领域 2024-11-30