耐化学 PVDF 法国阿科玛 2800-00 抗应力开裂 热稳定 电线电缆 管件 片材应用

Kynar Flex® 2800-00

Polyvinylidene Fluoride

Arkema

产品说明：

KYNAR FLEX® 2800-00 is a pelletized, semi-crystalline VF 2 based copolymer. KYNAR FLEX® 2800-00 has been specifically designed for use in wire and cable constructions and other uses requiring high flexibility and improved resistance to impact. For chemical applications, it can be extruded into sheets and tubing. KYNAR FLEX® 2800-00 can be injection molded.

ADVANTAGES:
Improved flexibility at subzero temperatures to -20°C(-4°F)
Improved stress crack resistance to -20°C(-4°F)
Improved elongation at break

ADDITIONAL CHARACTERISTICS:
Easy processability using conventional equipment
Excellent thermal stability
Excellent chemical resistance
Retains properties after aging
Meets UL 910 smoke and flame requirements as cable jacket
UL temperature rating 125°C
Radiation crosslinking

物性信息：

基本信息

黄卡编号	E54699-244851
特性	低温下的柔性 高 ESCR（抗应力开裂） 抗撞击性，良好 可加工性，良好 良好的柔韧性 耐化学性良好 热稳定性，良好
用途	电线电缆应用 管件 片材

形式	粒子
加工方法	挤出 注射成型
多点数据	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

物理性能额定值单位制测试方法

比重	1.77 到 1.80	g/cm³	ASTM D792

硬度额定值单位制测试方法

肖氏硬度 (邵氏 D, 23°C)	60 到 70		ASTM D2240

机械性能额定值单位制测试方法

抗张强度			ASTM D638
屈服, 23°C	20.0 到 34.5	MPa	ASTM D638
断裂, 23°C	17.2 到 34.5	MPa	ASTM D638
伸长率 (断裂, 23°C)	100 到 300	%	ASTM D638
弯曲模量 (23°C)	483 到 758	MPa	ASTM D790
弯曲强度 (23°C)	20.7 到 34.5	MPa	ASTM D790
压缩强度 (23°C)	31.0 到 41.4	MPa	ASTM D695

热性能额定值单位制测试方法

熔融峰值温度	140 到 145	°C	ASTM D3418

电气性能额定值单位制测试方法

体积电阻率 1(20°C)	2.0E+14	ohms·cm	ASTM D257

充模分析额定值单位制测试方法

熔体粘度 (232°C, 100 sec^-1)	2200 到 2700	Pa·s	ASTM D3835