高刚性 PEI 基础创新塑料(美国) EFL-4036 耐磨 电气领域应用

LNP Lubricomp® EFL-4036 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant

Polyetherimide (PEI)

产品说明：

Features: Lubricated

Forms: Pellets

Processing Method: Injection Molding

Information provided by LNP, a GE Plastics Company.

This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

比重	1.62 g/cc	1.62 g/cc	Method A; ASTM D792
密度	1.62 g/cc	0.0585 lb/in³	ISO 1183
吸水率	0.10 %	0.10 %	at 24 hrs; ASTM D570
线性成型收缩率	0.0020 cm/cm	0.0020 in/in	ASTM D955
线性成型收缩率，横向	0.0050 cm/cm	0.0050 in/in	ASTM D955

机械性能额定值 (公制)额定值 (英制)测试方法

抗张强度(断裂)	175 MPa	25400 psi	ASTM D638
伸长率 (断裂)	2.0 %	2.0 %	ASTM D638
拉伸模量	12.7 GPa	1840 ksi	ASTM D638
弯曲强度	248 MPa	36000 psi	ASTM D790
弯曲模量	11.3 GPa	1640 ksi	ASTM D790
悬壁梁缺口冲击强度	1.23 J/cm @Thickness 3.18 mm	2.30 ft-lb/in @Thickness 0.125 in	ASTM D256
悬壁梁无缺口冲击强度	7.10 J/cm @Thickness 3.18 mm	13.3 ft-lb/in @Thickness 0.125 in	ASTM D256
悬壁梁缺口冲击强度	13.1 kJ/m²	6.23 ft-lb/in²	ISO 180
悬壁梁无缺口冲击强度	46.9 kJ/m²	22.3 ft-lb/in²	ISO 180
Falling Dart Impact	10.3 J	7.60 ft-lb	ASTM D3763
冲击试验	3.65 J	2.69 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2
动态摩擦系数	0.46	0.46	vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
静态摩擦系数	0.43	0.43	vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor	70.5 x 10-8 mm³/N-M	35.0 x 10-10 in³-min/ft-lb-hr	40psi, 50ft/min; tested in accordance with LNP WI-0687

热性能额定值 (公制)额定值 (英制)测试方法

载荷下热变形温度(1.8 MPa)	199 °C	390 °F	Unannealed; ASTM D648

加工性能额定值 (公制)额定值 (英制)测试方法

加工（熔体）温度	360 - 366 °C	680 - 691 °F
模具温度	121 - 149 °C	250 - 300 °F
干燥温度	121 - 149 °C	250 - 300 °F
干燥时间	4 hour	4 hour
水分含量	0.020 %	0.020 %	Suggested